Para Aramid Staple Fiber Filament Yarn
The most prominent properties of the Para Aramid are its high strength, high modulus and heat resistance. For Para Aramid, ratio of weight/strength is 6 times of steel wire, 3 times of glass fiber and twice of high-strength nylon. Ratio of weight / modulus is 3 times of steel wire, twice of glass fiber and 10 times of high strength nylon. Para Aramid can keep 95% strength after working for 500 hours at 160°C and keeps 75% strength after working for 100 hours at 200°C. Para Aramid is often used as a special structure material with properties of light weight, heat-resistant.
Application
Classification | Example | Characteristics |
Tire | Aircraft, Racing care tire, High speed tire, Heavy loaded tire, Motorcycle tire, Bicycle tire | Light weight, High strength, High modulus, Dimensional Stability, Low Shrinkage |
Mechanical rubber rope | Convey belt, Transmission belt, Automotive hose, Hydraulic hose, Marine exploration hoses, oil and gas pipelines | High strength, High modulus, Dimensional stability, Heat resistance, Chemical resistance |
Cable rope | Aerial optical fiber cable, Duct cable, General cable, Mechanical structure cable, Marine cable, Military cable, Parachute code | High strength, High modulus, Dimensional stability, Low density, Corrosion resistance, Good dielectric properties, Heat resistance |
Composite material | Aerospace structure, Container structure, pressure vessel, ship structure, sports and recreation apparatus, plastic additive, coated fabric | Light weight, High strength, High modulus, resistance to impact, abrasion resistance |
Life protection | Bulletproof vest, Helmet, Bulletproof armor, Transport protection, Strategic facilities protection, Explosive ordnanced disposal clothing, Stab resistant clothing | High strength, Good energy dissipation, Light weight, comfort |
Friction and sealing | Brake lining belt, Clutch lining, seal pad, packing, Thixotropy additive, Industrial paper | Fiber fibrillation, Heat-resistance, corrosion resistance, Flame retardant, good mechanical properties |
Safety protection | Heat resistant work clothes, fire prevention blanket, flame retardant textile, cut resistant glove, cut resistant seat fabric | Heat resistance, flame retardant, Anti-cut |
Civil engineering | Concrete reinforcement, Maintenance and reinforce building, bridge and road | Light weight, High Strength, Corrosion resistance, non magnetic, non conductive |
Electronic communication | Special printed circuit board, electronic and electrical appliance structural parts, airborne satellite radar cover, wave-transmitting structural materials, light antenna | Light weight, High modulus, Good wave-transmitting, Heat durable |
Specification
Filament
Type | Item (dtex/f) | Finish | Description |
YHTF100 | 440dtex/267f 830dtex/500f 1110dtex/666f 1680dtex/1000f 2200dtex/1000f | Regular | Standard A grade |
YHTF110 | 1110dtex/666f 1680dtex/1000f | Customize | Standard A grade |
Staple
Type | Item (length/dtex) | Finish | Description |
YHTF300 | 38mm/1.68-2.52dtex 51mm/1.68-2.52dtex 60mm/1.68-2.52dtex | Regular | Standard High Strength A grade |
Short Staple
Type | Item (dtex/f) | Finish | Description |
YHTF400 | 3mm 6mm | No | Straight |
YHTF410 | 6mm | No | Curly |
Pulp
Type | Item (dtex/f) | Finish | Description |
YHTF500 | 0.8mm 2mm 3mm | No | Dry |
YHTF510 | 0.8mm 2mm | No | Wet |
Physical Properties
Item | Unit | Index |
Monofilament | dpf | 1.5-2.5 |
CV | % | ±2.0 |
Density | g/cm3 | 1.44 |
Moisture Regain (1) | % | 4.5 |
(1) 24°C, 55% RH | ASTM D885 (Ref.) GB/T 19975-2005 | |
Strength | cN/dtex | ≥20.0 |
Initial modulus | cN/dtex | ≥490 |
Elongation | % | 2-4 |
Shrinkage | ||
(Water) 100°C | % | <0.1 |
(Air) 177°C | % | <0.1 |
Heat Shrinkable stress | ||
(Air) 177°C | cN/dtex | <0.88 |
25°C | J/(kg x K) | 1420 |
100°C | J/(kg x K) | 2010 |
180°C | J/(kg x K) | 2515 |
LOI | % | 29 |
Decomposition temperature | °C | 550 |
Long-term use temperature range (Air) | °C | 149-180 |
Heat of combustion | °C | 35x106 |
Para Aramid Staple Fiber Filament Yarn